Seamed sleeved blanket and method for making and using same

ABSTRACT

A gapped or seamed cylindrical offset printing blanket having pre-made blanket material mounted on a cylindrical sleeve, and a method for making same, are disclosed, wherein conventional, manufactured blanket material in flat form made by methods known in the art is adhered to a cylindrical sleeve to economically produce a blanket. The leading and trailing ends of the flat blanket material are joined in close proximity such that a small gap is formed. A seam may be made with a filler material that fills the remaining gap resulting in a seamed sleeved blanket. In use, the seam is aligned with non-print area on the adjacent printing plate, or the adjacent plate cylinder gap of the printing press. Being narrower than the plate cylinder gap, no loss of print length results from the seam.

The present application is a section 371 of international applicationPCT/US00/28379, filed Oct. 13, 2000, which is a continuation-in-part ofU.S. patent application Ser. No. 09/419,493 , filed Oct. 15, 1999 nowabandoned.

BACKGROUND OF THE INVENTION

Prior art seamless cylindrical or sleeved offset printing blankettechnology is well known in the industry and documented in severalpatents, for example, those assigned to Heidelberg Harris (U.S. Pat.Nos. 5,323,702; 5,429,048; 5,440,981; 5,553,541; 5,535,674 and5,654,100) and to Reeves Brothers Inc. (U.S. Pat. No. 5,522,315) thecontents of all of which patents are hereby incorporated by reference.Two examples of the prior art seamless sleeved blanket 10 areillustrated in the schematic drawings of FIGS. 1 to 3. FIGS. 2 and 3 aretaken in sections parallel to the circular end of the roll. For ease ofillustration, the curvature of the roll has not been shown. The FIG. 2version 10A contains two windings of spiral wound thread 12A and istypical of blankets produced by Reeves and Day (for the Heidelbergpresses). The 10A version also has a sleeve 14A, usually of nickel, thespiral wrapped threads 12A, a compressible layer 16A made of typically arubber containing microspheres, a reinforcing layer 18A carrying anotherroll of spiral wrapped threads 12A, made of rubber with threads beingcotton, polyester or other materials, and the printing layer 20A havinga printing face 22A. Of course, the blanket including its sleeveactually curve around forming a continuous cylinder. FIG. 3 showing theversion 10B, contains only one winding of spiral thread 12A and includesa thick rubber base layer 14B. This construction is typical of Sumitomoproduced sleeves for use on Mitsubishi presses. This seamlesscylindrical sleeve has the inner nickel sleeve 16B, a compressible layer18B which can be joined to the base 14B by an adhesive layer 20B. Aprinting layer 22B is provided and has a printing face 24B. Again, thesleeve 10B actually curves around to form a seamless cylinder as shownin FIG. 1.

In the prior art, cylindrical offset sleeved printing blankets, such asdiscussed above, are produced by spiral winding carrier and reinforcingthreads 12A/12B helically around a continuous sleeve 24A/16B. The sleeveis usually coated with an adhesion promoting primer. A first layer ofpolymeric coated thread is spiral wound onto the coated sleeve bypassing the thread through a dip tank containing the solvated anduncured polymeric material as it is spiraled around the rotating sleeve.Dispersed in the polymeric material of this first layer are hollowmicrospheres that provide compressibility to the finished blanket. Theamount of the coating is typically controlled as the thread exits thedip tank through a restrictive opening which must be large enough toallow the microspheres to pass through while small enough to preventexcessive coating and the resulting inability to dry and set thepolymeric material before sagging can occur. The coating is relativelythick such that the solvents must be evaporated very slowly prior tocuring to prevent trapped gasses from blowing unwanted voids in thefinished layer. The long evaporation time tends to slow down theproduction rate. The polymeric material is then cured. The resultingcompressible layer is very rough, uneven and overbuilt, requiringgrinding to the required dimensions.

The polymeric material applied by this method tends to maintain its formaround the diameter of the thread resulting in unfilled valleys betweenthis layer and the coated sleeve. This unfilled area leads to gauge loss(thickness or diameter loss of a finished blanket sleeve—which canresult in loss of printing contact) in the finished product and issometimes compensated for by carrying out the additional steps byspreading a filling layer of solvated polymeric material onto the coatedsleeve with a doctor blade set up prior to winding of the coatedthreads. Of course, all of the polymeric material may be applied with adoctor blade set up, as a calendered sheet or other methods known to theart and the threads omitted or spiraled around or under the appliedpolymeric layer.

After grinding the first inner layer to the required dimensions, asecond outer layer of polymeric coated thread is wound around the sleevein a similar fashion to the first layer; however, microspheres are notincluded. This layer serves as a reinforcing layer and stabilizes theoverformed printing surface. Again, the polymeric material may also beapplied with a doctor blade set up, as a calendered sheet or othermethod known to the art and the threads omitted or spiraled around orunder the thus applied polymeric layer.

The overlaid printing surface may be applied as a solvated polymericcompound utilizing a doctor blade set up or as a solid by severalmethods known to the art such as any known extrusion or calenderingprocess. The completed composite is cross wrapped or otherwise held inplace, then cured with pressure applied to the outer layer by severalmethods known to the art to mold and adhere all layers together. In thefinal step the cured composite is again ground to the requireddimensions in such a way as to provide a surface profile conducive toink transfer.

This process results in a cylindrical offset printing blanket that iscompletely seamless throughout all of its layers but requires every stepto be carefully performed on an individual, sleeve by sleeve basis.Efficiencies associated with mass batching of component parts are verylimited, if not impossible. It has also been found that cylindricaloffset printing blankets produced by this method tend to draw in thewidth, wrinkle or crease the paper web during use resulting inunacceptable side to side registration through successive printingunits. In the prior art, to overcome this deficiency the compressiblelayer is profiled in a convex manner during the grinding operation toprovide a spreading effect on the paper web, further requiring theindividual processing of each sleeve during this step in themanufacturing process.

SUMMARY OF THE INVENTION

This invention utilizes a pre,made or pre-manufactured, unitary flatoffset printing blanket made by any of the methods known to the art offlat offset printing blanket manufacturing to produce, in mass, aunitized composite blanket covering which can be applied, in a seamedfashion, to a continuous supporting sleeve, such that the seam has anegligible effect on print length and gap bounce. The pre-made blanketmaterial will contain requisite reinforcements which are generally layedout in a rectangular manner, and are not spiral wound. The seam ispreferably parallel to the longitudinal axis of the sleeve and notskewed ideally by more than {fraction (1/16)} ″of inch for a plate of{fraction (1/16)} ″of inch plate gap to avoid registration and printlength issues. For other size plate gaps one could use other tolerancebut preferably not larger than the plate gap. The opposing ends of theflat blanket should butt together as closely as possible but preferablyleave some gap to provide a good fit should cut blanket lengths vary,and the resulting gap should preferably be narrower than the plate gapof the press for which the sleeve is designed if it is to be aligned inthat manner. In this way, the two gaps (one in the blanket—the other onthe press plate cylinder) can be aligned during use so that there is noloss of print area or it is limited to the plate gap area.Alternatively, the seam can be made to coincide with any non-utilizedarea of a plate cylinder, such as, for example, in the trim margins ofadjacent print areas.

The invention may include a blanket index, location or locking system orthe like, which could use a pin and opening or other mechanism andinsures that the blanket and plate gap (or other chosen area) alwaysmatch perfectly. Preferably, the gap between the opposing ends of theblanket can be filled with a resilient and solvent resistant compound tominimize gap bounce and especially to prevent water and solvents fromwicking into the ends of the blanket. If this wicking is not prevented,swelling and delamination would be expected to occur.

In use, installation time is maintained at a minimum by providing ablanket in cylindrical or sleeve form when installed on the press'sblanket cylinder. By utilizing flat blanket technology, there is no needfor special profiling to spread the paper web. The unitized compositeblanket covering may also be purchased as a standard material availablefrom any number of offset printing blanket manufacturers and applied toa continuous supporting sleeve according to the method of thisinvention.

The sleeve could be made of metallic, for example, nickel or steel, ornon-metallic construction, say a solid, laminate or winding of films,such as mylar or thermoplastics. The use of a non-metallic sleeve ispossible as there is no need to vulcanize or subject the product to highheat to cure during manufacture.

OBJECTS OF THE PRESENT INVENTION

It is the object of this invention to provide a seamed offset printingblanket that maintains the benefits of the prior art (maximized printlength, minimized gap bounce and reduced installation time) whilereducing manufacturing time and expense.

It is an object of the present invention to provide a seamed sleevedblanket for a printing press.

It is another object of the present invention to provide a method formaking a seamed sleeved blanket for a printing press.

It is yet another object of the present invention is to provide a methodfor using the seamed sleeved blanket of the present invention.

A still further object of the present invention is to provide a seamedsleeved blanket in combination with a printing press.

Yet a further object of the present invention is to provide acombination of seamed sleeved blanket, printing press and indexing,locating or locking system.

Another object is to provide a seamed sleeved blanket which can utilizea non-metallic sleeve.

These and other objects of the present invention will become apparentfrom the following specification and accompanying drawings.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a schematic view of a prior art seamless blanket showing wherethe sections shown in FIGS. 2 and 3 are taken along the lines 2/3—2/3(the slash meaning “or”).

FIG. 2 is a cross-sectional view of a segment of a prior art seamlesssleeved blanket with the actual curvature being omitted for simplicity.

FIG. 3 is a cross-sectional view of a segment of a second prior artseamless sleeved blanket with the curvature being omitted forsimplicity.

FIG. 4 is a schematic view of the seamed blanket of the presentinvention n showing where the section shown in FIG. 5 is taken along thefines 5—5.

FIG. 5 is a cross-sectional view of a segment of an embodiment of seamed blanket of the present invention with the curvature being omitted forsimplicity.

FIG. 6 is a schematic view indicating how a sheet of thepre-manufactured blanket material is wrapped around the sleeve to makethe seamed sleeved blanket of the present invention.

FIG. 7 is a perspective view of the sleeve of the present inventionshowing how it may be notched to index or lock it into place withrespect to a press's blanket cylinder.

DESCRIPTION OF THE PREFERRED EMBODIMENT

A schematic drawing of the seamed sleeved blanket 40 produced accordingto this invention can be seen in FIGS. 4 through 7. As shown in FIG. 6,according to this invention a conventional, flat offset printing blanketmaterial 42 may be manufactured by methods well known to the art orpurchased in roll form and cut to specific dimensions so that it can bewrapped (as indicated by the large arrows) as a solid sheet around acontinuous supporting sleeve 44 to produce the seamed sleeved blanket 40of the present invention and shown in FIG. 4, the gap or sewn beinggiven numeral 45. Referring to FIG. 5, preferably the followingconstruction method can be used. The blanket material 42 could be of anydesired commercially available structure and could have a rubber surface46, say 0.023 inches thick over a first outer fabric layer 48(reinforcement), say 0.009 inches thick, over a compressible layer 50,say 0.014 inches thick, over a middle fabric layer 52 (reinforcement),say 0.011 inches thick, over an adhesive layer 54, say 0.0002 inchesthick, over an inner fabric layer 56 (reinforcement), say 0.015 inchesthick. The sleeve could be metallic or nonmetallic, and if metallic,preferably of nickel. The expandable nickel sleeve has been the sleeveof choice for sleeve offset blankets. There are alternative materialsthat can be used such as fiberglass, kevlar, plastic, and/or apolyethylene (PET) sleeve. Some of these materials and particularly PEThave several advantages over the nickel: lower cost, safer for theoperator (no sharp edges), more durable than nickel in the manufacturingand pressroom environment. While the reinforcement shown was fabric,other conventional reinforcements could also be used. The sleeve 44would be treated with a primer 58, say 0.002 inches thick, and coveredwith a urethane or other adhesive 60, say 0.002 inches thick, that bondsor adheres the blanket material 42 to the sleeve 44. The across the rolldimension may be cut equal to or less than the length of the sleeve 44and the around or circumferencial dimension may be cut equal to or nomore than {fraction (1/16)} ″less than the outer surface length orcircumference of the sleeve for use on a press with a plate gap of{fraction (1/16)} of an inch. Of course, for other size plate gaps, thisdimension could very. The ends 62 and 64 (of FIG. 4) of the flat blanketmaterial 42 may also be cut or skived at an angle so that the ends meetin the seam 45 (indicated by the heavy double arrow in FIG. 5) generallyflush from top 68 (outer surface) to bottom 70 (inner surface) (see FIG.5) when wrapped around the sleeve 44. The roll goods from which the cutsare made may be of any length and width common in the industry butshould be maximized to provide the greatest number of cuts possiblewithout excessive cutting waste. Manufacturing or purchasing in thisform takes advantage of the efficiencies associated with massproduction. It is well known that the wider and longer a roll ofprinting blanket material is produced, the less the cost per unit area.

The requirements of the flat offset printing blanket material 42 are thesame as for any offset printing blanket and may vary according to thespecific end use. A typical blanket physicals are: compressible layer0.008 to 0.014 thick, stretch less the 1.25%, ply adhesion>2 lbs./linearinch, tensile stretch>300 pounds/linear inch, Shore A Durometer 70-85.Additionally, the printing face 72 usually will be overbuilt forgrinding of the finished product to the required dimensions. Thepreferred printing blanket construction according to this invention isone containing one or more, but preferably, three plies 48, 52 and 56 ofreinforcing fabric bonded together with an adhesive or solvent polymericresistant cement, preferably a nitrile cement is used. Alternatively,nonwovens, films or other supporting substrate, could be used instead offabric. As the blanket material was pre-manufactured, the reinforcementgenerally will not be spiral wound but will run parallel andperpendicular at right angles to the center axis of the blanket cylinderaxis and/or the axis of the blanket sleeve when installed on the blanketcylinder. It is believed that the absence of non-spiral windings in thepresent invention is beneficial to printing, keeping registration andavoiding web draw in. The blanket material should preferably contain acompressible or foam layer 50 between the two upper fabric plies 48 and52 that is uniform in thickness across the width. This carcassconstruction should be in a range of 0.025 to 0.070, and preferably,approximately 0.055 inches in thickness. Of course other thickness couldbe used. A solvent resistant polymeric printing face 46 preferably madeof nitrile or nitrile blends with other polymers is applied over the topply of fabric and should be in a range of 0.010 to 0.070 and preferablyno less than 0.044 inches thick so that the total gauge of the finishedflat blanket is in a range of 0.030 to 0.110 and preferablyapproximately 0.096 inches thick.

After the individual pieces of blanket material 42 are cut to theappropriate size to fit around the sleeve, they are dried in an oven,for about 30 minutes at, for example, 150° F. to remove moisture orotherwise treated to remove moisture. Note, the blankets' sleeve is notsubject to this drying, malting the use of many non-metallic sleevematerials possible. The dried or moisture free blanket 42 is coated witha thin layer of self-curing polymeric material, preferably urethane 54such as Por-A-Mold S-2868 manufactured by Synair. These self-curingurethanes are hindered by water so that moisture left in the blanketmaterial 42 will prevent adequate cure and adhesion. The coated blanketis then wrapped around the sleeve 44. The sleeve 44 has a thicknessranging from 0.002 to 0.010, and preferably 0.005 inches thick. Thecontinuous sleeve may be made of suitable expandable or stretchablemetal, and preferably nickel. The sleeve and completed blanket should beexpandable or stretchable as that is the usual manner in which they areinstalled on a blanket cylinder. That is, the sleeve is expanded orstretched with air pressure to permit it to be so installed.

Other bonding materials may be used but often require heat activation.Application of heat to the already cured flat blanket can degrade itsphysical properties.

Nickel sleeves 22 are preferred but any sleeve, made of a rigid orsemi-rigid material and having a Youngs Moduus and thickness that allowsit to be expanded sufficiently to slip over the printing cylinder duringinstallation and removal while retracting to fit the outer diameter ofthe cylinder tightly during use, may be used. As noted, it is possibleto use non-metallic materials for the sleeve in the present invention asthe sleeve never need be exposed to high temperatures. The sleevedimensions must be chosen so that the interference between the insidediameter of the sleeve and the outside diameter of the printing cylinderon which it will be mounted prevents slippage around the cylinder duringuse. For example, 0.005 inch thick nickel sleeve should have an insidediameter of 0.002 to 0.020 less than the outside diameter of the blanketcylinder on which it will be mounted.

The sleeve 22 is first treated and primed (see FIG. 5, numeral 58) in amanner common to the art and further coated with the self-curingurethane. The preferred primer is a single coat primer such as Pliogrip6025, marketed by Ashland Chemical. Two coat primer systems may also beused.

The urethane or other coating is preferably applied to the back of theflat blanket by a doctor blade to completely fill the interstices of thefabric backing increasing the overall blanket thickness minimally or notat all. The urethane coating is applied to the sleeve by brushing butmay also be applied by dipping, spreading with a doctor blade, sprayingor other methods known to the art. The adhesive thickness may varydepending on the adhesive system used and should be consistent with theadhesive manufacturer's directions.

Hydrogenated nitrile rubber compounds have been successfully used inplace of the urethane as solvated and spread adhesives or as calenderedadhesive sheets. This method requires curing of the completed compositeunder pressure and at elevated temperatures while the urethane can becured at room temperature. Of course, there are many other non-rigidadhesives that can be used to bond the blanket to the sleeve, such asacrylics or rubber based adhesives. They are only limited by the needfor solvent and water resistance.

The ends 62 and 64 of the blanket are butted to each other such that thejoint or seam 45 runs preferably parallel to the longitudinal axis ofthe sleeve. This butt joint should not be skewed by more than {fraction(1/16)} ″to prevent misregistration (see discussion above), short print,walking, or unacceptable movement of the printed web.

While being manufactured, to bold the flat blanket material in place onthe sleeve, it may be secured in place with clamps and spiral wrappedwith mylar or other tape under controlled tension (2-10 lbs./in.),removing the clamps as the tape spiral traverses the length of thesleeve. The mylar or other tape is butt or spiral would in such a waythat successive wraps overlap one another sufficiently (5 to95%—preferably, 40 to 60%) to apply pressure to the entire surface ofthe blanket. Alternatively, the blanket may be secured with adhesivetape prior to wrapping with mylar and/or the entire blanket may beenclosed in a mold that simultaneously holds the blanket in position andapplies the appropriate pressure. The self-curing urethane cures andbonds the flat blanket to the primed nickel sleeve within 24 hours atroom temperature. This cure rate can be accelerated with exposure toelevated temperatures, so long as those temperatures do not degrade theproduct. 150° F. is a good curing temperature that would reduce the curetime to about 8 hours. The mylar tape or mold is then removed.

This invention includes the concept of using a manufacturing fixture ormold to improve the manufacturing quality of the blankets. The idea isto use a device such as a manufacturing fixture or a mold that wouldallow the seam to be located, aligned precisely, and securely heldduring the curing process. The fixture would also apply even pressure onthe surface of the blanket after it has been wrapped around the tubularsleeve. This replaces the manual method of “wrapping” the blanket priorto curing the bonding agent. The result is that the blanket quality canbe reproduced consistently. The skill level of the manufacturing personis not as critical. It will also lend to automating the entiremanufacturing process in order to reduce the cost and increase thequality. For example, the mold or fixture would be generally “C” shapedin cross-section and closed by over center clamps that pull the mold orfixture closed. That is, the “C” closes upon itself to form an “O”, withthe blanket material sleeve in the center of the “O”. After the materialcures, the blanket sleeve is released from the mold and finished, as bygrinding on its outer surface.

The remaining gap 45, if any, between the opposing ends of the blanket,can be filled with the urethane or nitrite material and allowed to cureadhering the two ends together and providing a suitable surface. The gap45 should be filled with a resilient and solvent resistant compound tominimize gap bounce and to prevent water and solvents from wicking intothe ends of the blanket. Of course, if the ends 62 and 64 are really aclose fit or touching, then only sealing may be needed to preventwicking, any such small or negligible gap not needing further filling.

It is also preferred that when used the gap filler material be of adifferent color from the blanket face so that the seam location iseasily identified for proper alignment during installation. The sameurethane is also utilized to seal the blanket materials 42 edges andprevent wicking into the sides of the blanket. The different color seamand a mark on the blanket cylinder could form part of an indexing systemfor properly locating the seam. Of course, another indicator than theseam could also be placed on the blanket cylinder and used with anappropriate mark on the blanket cylinder for indexing purposes.

Grinding to the appropriate diameter and surface roughness finishes thecomposite seamed cylindrical blanket. The diameter is specific to thepress on which the sleeve will be used should be such that, incombination with the blanket's compressibility, excessive pressure doesnot cause slippage around the print cylinder. The appropriate surfaceroughness is achieved by selection of the face compound and grindingmedia. The “roughness average” (Ra) should be in the range of 0.2 to 2.0microinches.

Prior art cylindrical blankets are typically built with a minimallythick composite covering the nickel sleeve. This results in excessiveheat transfer to the cylinders on which they are mounted. Duringgrinding, the heat transfer to the grinding mandrel can causedistortions requiring two stage or wet grinding. The blanket is firstrough ground, allowed to cool and then finished. The thickness of thecomposite covering of this invention is such that heat transfer isnegligible. Grinding may be accomplished in a single step and withoutthe mess or capital expense associated with wet grinding.

According to this invention, multiple flat blanket pieces may be seamedtogether on a single sleeve for use on presses having multiple printingplates and thus multiple plate gaps. Such a blanket would have seamscorresponding to the plate gaps and could be made to register with them.Also, according to the present invention any seam or seams on thesleeved blanket could be set up to fall in any corresponding area on theplate cylinder that did not interfere with useful printing.

The use of a mold to hold the flat blanket in position and applypressure while the urethane cures allows for the possibility of usingpre-ground or cast face blanket coverings. The impressions left by curetapes/wraps require grinding of the finished sleeve, while the use of amold leaves no such impressions. In this method, the gauge of the flatblanket material 42 covering and the outside diameter of the nickelsleeve control the outside diameter of the finished sleeve. Surfaceprofiles are imparted in mass to the rolls of flat blanket materialprior to cutting by methods well known to the art and reduce anotherunit by unit processing step.

The manufacturing costs associated with the prior art are high and theprocess is very slow. Output from the method of the present invention isthree to four times higher than that of the prior art. And much of theauxiliary equipment such as blanket curing ovens, winding lathes, etc.,are not needed. Production or purchasing of the blanket materialcovering in roll or flat form and large quantity significantly reducesthe cost and individual seamed sleeves of the present invention can becompleted at a rate of at least one every hour on the same machinerywithout the auxiliary equipment.

Unit to unit variations are common in the prior art. According to thisinvention, all seamed sleeves of the present invention produced from thesame master roll of flat blanket material will be very consistent inproperties.

In the prior art, there are no reinforcing or stabilizing threads in thehorizontal direction. The threads applied in the circumferencialdirection are not parallel to the end plane of the sleeve. It ispossible that this thread orientation is responsible for the tendency todraw in the paper web during use and the consequent side to sidemisregistration from printing unit to printing unit. The seamedcylindrical blanket of this invention provides threads bothperpendicular and parallel to the axis of the sleeve and no suchregistration shift issues occur. The need for profiling the compressiblelayer is not necessary.

Prior art seamless, sleeved or cylindrical blankets have historicallyslipped fractionally around the printing cylinder during use whichcauses print distortion. The proper combination of the blanketcompressibility and finished outside diameter of the secured sleevedblanket of the present invention has been found to eliminate thisslippage.

In addition, sleeves may be used in the invention that are made ofplastic, rubber, fiberglass, kevlar or other suitable materials havingappropriate elasticity characteristics. Since our invention requires nofinal vulcanization process, sleeve materials with softening point lessthan 300° F. can now be considered for use. This was not possible withcylindrical blanket made by the prior art.

This invention also provides for a sleeve to blanket cylinder lock upsystem. The lock up system guarantees that once the blanket is installedif will not slip circumferentially or axially on the blanket cylinder.This movement has been a problem with prior art. For example, a notch oropening 80 could be provided in the sleeve which cooperates with araised portion or pin 82 (indicated in dashed lines in FIG. 7) on theplate cylinder. Other suitable two part mechanisms or male and femaleportions that fit together could also be used, one in the sleeve withthe other in the plate cylinder. Should a full locking system not bedesired or needed, the sleeve and plate cylinder could be provided withappropriate indexing marks to locate the seam in the desired area, be itin the plate gap or other non- utilized non-printing area of the plateon the plate cylinder of the press.

While the preferred form of seamed, sleeved blanket and method of makingand using the same of the present invention have been disclosed anddescribed, it should be understood that other equivalent steps andelements of those called for in the below claims fall within the scopeof the appended claims.

1. A method for making a gapped sleeved blanket for a printing pressutilizing pre-made blanket material and a cylindrical sleeve having anouter circumference and an outer circumferential surface, comprising thesteps of: cutting the pre-made blanket material to a length about thatof the outer circumference of the cylindrical sleeve, placing thepre-made blanket material around the outer circumference of thecylindrical sleeve, bringing the opposite ends of the pre-made blanketmaterial towards each other to have them lie adjacent each other to forma gap on the outer circumference of the cylindrical sleeve, and adheringthe pre-made blanket material to the outer circumferential surface ofthe cylindrical sleeve.
 2. The method of claim 1, comprising the furtherstep of priming the outer circumferential surface of the cylindricalsleeve prior to the step of adhering the pre-made blanket material tothe cylindrical sleeve.
 3. The method of claim 2, comprising the step ofapplying a urethane adhesive to the primed cylindrical sleeve beforecarrying out the step of bringing the opposite ends of the pre-madeblanket material toward each other to have them lie adjacent each otherto form the gap.
 4. The method claim 3: wherein said pre-made blanketmaterial has a thickness of 0.030 to 0.110 inches thick and wherein saidcylindrical sleeve has a thickness of 0.002 to 0.010 inches thick, andwherein said pre-made blanket material has at least one reinforced layerthereon, comprising the steps of: filling the gap with material to forma seam, and finishing the blanket material and said seam to a desireddimension.
 5. The method of claim 1, wherein said cutting step comprisescutting the blanket material at one or more angles so that the cut edgesof blanket material lay close together when wrapped around said sleeve.6. The method of claim 1, comprising the further step of filling the gapbetween the opposite ends of the pre-made blanket material with fillerto form a seam.
 7. The method of claim 6, comprising the step offinishing the pre-made blanket material and the filler to have about thesame outer radial dimension.
 8. The method of claim 1, comprising thestep of finishing the pre-made blanket material to have about the sameouter radial dimension.
 9. The method of claim 1, comprising providing apre-made blanket material of thickness of 0.030 to 0.110 inches thickand providing a metallic cylindrical sleeve of a thickness of 0.002 to0.010 inches thick.
 10. The method of claim 1, comprising the step ofproviding a non-metallic cylindrical sleeve.
 11. The method of claim 10,wherein the non-metallic cylindrical sleeve and pre-made blanketmaterial have a combined thickness of generally about the distancebetween that of the blanket cylinder and the printing surface of anadjacent plate on a plate cylinder of the printing press on which theseamed sleeved blanket is adapted to be used.
 12. The method of claim 1,wherein said pre-made blanket material has at least one reinforced layertherein.
 13. The method of claim 12, wherein said pre-made blanketmaterial has a reinforced layer with three fabric layers therein.
 14. Aseamed sleeved blanket for use on a printing press having a platecylinder with at least one plate cylinder gap, comprising an expandable,continuous, cylindrical sleeve, a sheet of pre-made blanket materialwrapped around the continuous, cylindrical sleeve wherein the edges ofthe pre-made blanket material form a gap about the width of the platecylinder gap or smaller, said pre-made blanket material having asupportive substrate, with a compressible layer, adhesive for attachingthe pre-made blanket material to the cylindrical sleeve and materialfilling the gap to form a seam, said adhesive and said material fillingsaid gap being capable of setting at below vulcanizing temperature andbelow 300° F.
 15. The seamed sleeved blanket as in claim 14, whereinsaid pre-made blanket material has axial exposed edges, said axialexposed edges of said pre-made blanket material being sealed.
 16. Theseamed sleeved blanket as in claim 14, wherein said material fillingsaid gap and said pre-made blanket material each have an outer surfaceabout the same outer radial dimension.
 17. The seamed sleeved blanket asin claim 14, wherein said pre-made blanket material is adhered to saidsleeve.
 18. The seamed sleeved blanket as in claim 14, wherein saidpre-made blanket material has at least one reinforcement layer and atleast one compression layer therein.
 19. The seamed sleeved blanket asin claim 14, wherein said pre-made blanket material has at least two ormore reinforcement layers therein.
 20. The seamed sleeved blanket as inclaim 14, wherein said pre-made blanket material has non-spiral woundreinforcement material therein.
 21. The seamed sleeved blanket as inclaim 14, wherein said cylindrical sleeve is made of a metal that can beelastically expanded to place the seamed sleeved blanket onto a blanketcylinder of a press.
 22. The seamed sleeved blanket as in claim 21,wherein said cylindrical sleeve is made at least partially of nickel.23. The seamed sleeved blanket as in claim 14, wherein said cylindricalsleeve is coated with a primer to increase the adherence of the pre-madeblanket material to the cylindrical sleeve.
 24. The seamed sleevedblanket as in claim 14, wherein said cylindrical sleeve is made of anon-metallic material that can be elastically expanded to place theseamed cylindrical sleeved blanket onto a blanket cylinder of a press.25. The seamed sleeved blanket as in claim 24, wherein said cylindricalsleeve is made of non-metallic material with one or more laminations orwrappings.
 26. The seamed sleeved blanket as in claim 14, wherein aurethane adhesive adheres said pre-made blanket material to saidcylindrical sleeve.
 27. The seamed sleeved blanket as in claim 14,wherein said pre-made blanket material is adhered to said cylindricalsleeve, and said material filling said gap is the same adhesive thatattaches said pre-made blanket to said cylindrical sleeve.
 28. Theseamed sleeved blanket as in claim 27, wherein said same adhesive isurethane adhesive.
 29. The seamed sleeved cylindrical blanket as inclaim 27, wherein said pre-made blanket material is from 0.030 to 0.110inches thick and said cylindrical sleeve is from 0.002 to 0.010 inchesthick.
 30. The seamed sleeved blanket as in claim 14, wherein saidpre-made blanket material is attached to said cylindrical sleeve, saidpre-made blanket material has at least one reinforcement layer therein,said cylindrical sleeve being made of a metal that can be elasticallyexpanded to place the seamed sleeved blanket onto a blanket cylinder ofthe printing press, said cylindrical sleeve being made at leastpartially of nickel, said cylindrical sleeve being coated with a primerto increase the adherence of the pre-made blanket material to thesleeve, and a urethane adhesive that adheres said pre-made blanketmaterial to said cylindrical sleeve and is also used to fill said gap.31. The method of using the seamed sleeved blanket of claim 14, whereinsaid printing press has a blanket cylinder and a plate cylinder with aplate cylinder gap, and a printing plate having leading and trailingends wrapped around said plate cylinder with said leading and trailingends tucked into said plate cylinder gap, with said printing platehaving a useable print area that excludes said leading and trailing endstucked into said plate cylinder gap, comprising the step of indexing theseam of the seamed sleeved blanket to not coincide with the useableprint area of the printing plate, and installing the seamed sleevedblanket on the blanket cylinder so that the seam does not align with theuseable print area of said printing plate.
 32. The method as in claim31, wherein said seam is indexed to align with said plate cylinder gap.33. The method as in claim 31, comprising the further step of lockingthe seamed sleeved blanket to the blanket cylinder.
 34. A printing pressin combination with the seamed sleeved cylindrical blanket of claim 14,wherein said printing press has a plate cylinder with a plate cylindergap, and a printing plate having leading and trailing ends wrappedaround said plate cylinder with said leading and trailing ends tuckedinto said plate cylinder gap, with said printing plate having a useableprinting area that excludes said leading and trailing ends tucked intosaid plate cylinder gap, a blanket cylinder, and locking means on saidprinting press to lock the position of said seamed sleeved blanket tosaid blanket cylinder so that said seam of said seamed sleeved blanketdoes not align with the useable print area on said printing plate. 35.The combination of claim 34, wherein said seam aligns with said platecylinder gap.
 36. The combination of claim 34, wherein said lockingmeans comprises a mechanism on said seamed sleeved blanket and acooperating mechanism on said blanket cylinder.
 37. The combination ofclaim 36, wherein one of said mechanisms is a male component and theother of said mechanisms is a female component, said male and femalecomponents locking and fitting together.
 38. The combination of claim37, wherein said male component is on said blanket cylinder and saidfemale component is on said seamed cylindrical sleeve.
 39. Thecombination of claim 36, wherein said locking means is a raised portionor pin on said blanket cylinder and a notch or opening formed in saidseamed cylindrical sleeve, said raised portion or pin being engagable insaid opening or notch to locate the cylindrical sleeve.
 40. A seamedsleeved blanket for use on a printing press having a plate with aprinting surface, comprising an elastically expandable continuouscylindrical sleeve, a sheet of pre-made blanket material wrapped aroundsaid continuous cylindrical sleeve to form a gap, said pre-made blanketmaterial having a supportive substrate with a compressible layer,adhesive for attaching the pre-made blanket material to said continuouscylindrical sleeve, said gap being filled with material to form a seam,said seam and said continuous cylindrical sleeve being adapted to belocated such that said seam does not contact said printing surface ofsaid plate, said adhesive and said material filling said gap beingcapable of setting at below vulcanizing temperature and below 300° F.41. The seamed blanket as in claim 40, wherein said seamed cylindricalsleeve is made of polyethylene.